Carbon nanotube array, material, electronic device, process for producing carbon nanotube array, and process for producing field effect transistor

ABSTRACT

In order to obtain a carbon nanotube array including no m-CNTs through simple steps using a mechanism that is different from thermocapillary flow, there are provided a process for producing a carbon nanotube array including (A) a step of preparing a carbon nanotube array in which m-CNTs and s-CNTs are horizontally aligned; (B) a step of forming an organic layer on the carbon nanotube array; (C) a step of applying voltage to the carbon nanotube array in a long axis direction of the carbon nanotubes constituting the carbon nanotube array in the air; and (D) a step of removing the organic layer, and a carbon nanotube array obtained by the process.

TECHNICAL FIELD

The present invention relates to a carbon nanotube array, a material, anelectronic device, a process for producing a carbon nanotube array, anda process for producing a field effect transistor. Priority is claimedon Japanese Patent Application No. 2014-40003, filed Mar. 1, 2014, thecontent of which is incorporated herein by reference.

The present invention particularly relates to a carbon nanotube array inwhich semiconducting carbon nanotubes are horizontally aligned densely,specifically at a density of 1 line/μm or more, and a process forproducing the same.

The present invention relates to a material formed with the carbonnanotube array, for example, an electronic material, an opticalmaterial, or an electrochemical material.

The present invention relates to an electronic device formed with thecarbon nanotube array, specifically, a field effect transistor (FET), asolar cell, a chemical sensor, a photosensor, an optical element, or aterahertz sensor.

BACKGROUND ART

A carbon nanotube, particularly, a semiconducting carbon nanotube(hereinafter, referred to as an “s-CNT” in some cases) is expected to beapplicable to next-generation devices due to superiority in electronicproperties, optical properties, mechanical properties, thermalproperties, and the like.

A method for selectively producing an s-CNT has been explored but amethod for selectively producing only an s-CNT has not been establishedyet.

Instead of the method for selectively producing only an s-CNT, a methodfor producing a carbon nanotube array constituted with only s-CNTs byselectively removing only m-CNTs from a carbon nanotube array havings-CNTs and metallic carbon nanotubes (hereinafter, referred to as“m-CNTs” in some cases) has currently been examined in terms ofpracticality.

NPL 1 discloses a method of “electrical breakdown”. This method is amethod of applying voltage to each carbon nanotube of a carbon nanotubearray having s-CNTs and m-CNTs in a long axis direction so as to allow acurrent to flow into only the m-CNTs. The m-CNT in which a current flowscan be locally burned out by self Joule heating. However, in thismethod, the length of the m-CNT that can be removed is 100 nm at most.Therefore, this method has a problem that the method is not applicableto a carbon nanotube array in which the length of each carbon nanotubeis long. In addition, in the case in which the method is applied to thecarbon nanotube array in which the length of each carbon nanotube islong, there arises a problem that even when the m-CNT is cut, the m-CNTremains after cutting.

NPL 2 discloses a method of using nanoscale thermocapillary flow. Inthis method, a thin film made of onlyα,α,α′-tris(4-hydroxyphenyl)-1-ethyl-4-isopropylbenzene is provided on acarbon nanotube array having s-CNTs and m-CNTs. Then, voltage is appliedto each carbon nanotube of the carbon nanotube array in the long axisdirection so as to allow a current to flow into only the m-CNT. Due toself Joule heating of the m-CNT, the thin film in the vicinity thereofis torn and/or broken by the thermocapillary flow. As a result, them-CNT is exposed. On the other hand, the s-CNT is present under the thinfilm. Then, the exposed m-CNT is removed by reactive ion etching (RIE,O₂/CF₄). Finally, the thin film is removed and thus a carbon nanotubearray including only the s-CNTs is obtained.

In the method disclosed in NPL 2, there is a problem that the step iscomplicated because it is required to provide a step of removing them-CNT by reactive ion etching and the like after a step of generatingthermocapillary flow.

In the method disclosed in NPL 2, since thermocapillary flow is used,the density of the s-CNTs in the carbon nanotube array is low (1 line/3μm). Therefore, there is another problem that properties required for anelectronic material formed with the carbon nanotube array cannot beobtained.

Further, in the method disclosed in NPL 2, there is still anotherproblem that the material for generating thermocapillary flow is limitedto α,α,α′-tris(4-hydroxyphenyl-1-ethyl-4-isopropylbenzene or the like.

CITATION LIST Non-Patent Literature

[NPL 1] P. G. Colins et al., Science 292, 706 (2001).

[NPL 2] S. H. Jin et al., Nat. Nanotechnol. 8, 347 (2013)

SUMMARY OF INVENTION Technical Problem

An object of the present invention is to provide a method for solvingthe above problems.

Specifically, an object of the present invention is to provide a processfor obtaining a carbon nanotube array including no m-CNTs obtained byremoving m-CNTs from a carbon nanotube array having s-CNTs and m-CNTsthrough simple steps using a mechanism that is different fromthermocapillary flow.

Another object of the present invention is to provide a carbon nanotubearray including no m-CNTs in which the density of s-CNTs is high.

Solution to Problem

The present inventors have found the following inventions.

<1> A carbon nanotube array according to an aspect of the presentinvention is a carbon nanotube array including no metallic carbonnanotubes in which semiconducting carbon nanotubes are horizontallyaligned at a density of 1 line/μm or more.

<2> In the above <1>, a density of the semiconducting carbon nanotubesmay be 1,000 lines/μm or more.

<3> In any one of the above <1> and <2>, a length of each semiconductingcarbon nanotube of the carbon nanotube array may be 10 μm or more. Thelength of each semiconducting carbon nanotube may be preferably 100 μmor more and more preferably 1,000 μm or more.

<4> In any one of the above <1> to <3>, in a case of forming a fieldeffect transistor (FET) with the carbon nanotube array, an ON/OFF ratioof the FET may be 10,000 or more. In addition, the ON/OFF ratio of theFET may be preferably 100,000 or more and more preferably 1,000,000 ormore.

<5> A material according to an aspect of the present invention is formedwith the carbon nanotube array according to any one of the above <1> to<4>. This material may be, for example, an electronic material, anoptical material, an electrochemical material, or the like.

<6> An electronic device according to an aspect of the present inventionis formed with the carbon nanotube array according to any one of theabove <1> to <4>. The electronic device may be, for example, a fieldeffect transistor (FET), a solar cell, a chemical sensor, a photosensor,an optical element, or a terahertz sensor.

<7> A process for producing a carbon nanotube array according to anaspect of the present invention includes: (A) a step of preparing acarbon nanotube array in which metallic carbon nanotubes andsemiconducting carbon nanotubes are horizontally aligned; (B) a step offorming an organic layer on the carbon nanotube array; (C) a step ofapplying voltage to the horizontally aligned carbon nanotube array in along axis direction of the carbon nanotubes constituting the carbonnanotube array in the air; and (D) a step of removing the organic layer.

<8> In the above <7>, the organic substance in the (B) step may have athermal diffusion coefficient of 2'10⁻⁷ m²/s or less. In addition, thethermal diffusion coefficient thereof may be preferably 1×10⁻⁷ m²/s orless and more preferably 0.2×10⁻⁷ m²/s or less.

<9> In any one of the above <7> and <8>, the organic layer in the (B)step may be a layer made of onlyα,α,α′-tris(4-hydroxyphenyl)-1-ethyl-4-isopopylbenzene or a layer madeof only poly(methyl methacrylate).

<10> In any one of the above <7> to <9>, the semiconducting carbonnanotubes may be horizontally aligned at a density of 1 line/μm or more.In addition, the semiconducting carbon nanotubes may be horizontallyaligned preferably at a density of 3 lines/μm or more, more preferablyat a density of 10 lines/μm or more, and most preferably at a density of30 lines/μm or more.

<11> In any one of the above <7> to <10>, a length of the semiconductingcarbon nanotube may be 10 μm or more. The length of the semiconductingcarbon nanotube may be preferably 100 μm or more and more preferably1,000 μm or more.

<12> A process for producing a field effect transistor (FET) accordingto an aspect of the present invention may he a process using a carbonnanotube array that is produced using the process for producing a carbonnanotube array according to any one of the above <7> to <11>. An ON/OFFratio of the field effect transistor may be 10,000 or more, preferably100,000 or more, and more preferably 1,000,000 or more.

Advantageous Effects of Invention

According to the present invention, it is possible to obtain a carbonnanotube array including no m-CNTs by removing m-CNTs from a carbonnanotube array having s-CNTs and m-CNTs through simple steps using amechanism that is different from thermocapillary flow.

In addition, according to the present invention, it is possible toobtain a carbon nanotube array including no m-CNTs in which the densityof s-CNTs is high.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a graph showing the ON/OFF ratio of a FET using a carbonnanotube array before a series of steps of applying voltage and removinga film are performed (“Before”) and after the steps are performed(“After”).

FIG. 2 is a schematic view when voltage is applied to a carbon nanotubearray including m-CNTs and s-CNTs.

FIG. 3 shows SEM images of the carbon nanotube array before a series ofsteps of applying voltage and removing a film are performed (“Before”)and after the steps are performed (“After”).

FIG. 4 shows SEM images of the carbon nanotube array before a series ofsteps of applying voltage and removing a film are performed (“Before”)and after the steps are performed (“After”) and a graph showingmeasurement results of spots shown in the SEM images using Ramanspectroscopy.

DESCRIPTION OF EMBODIMENTS

Hereinafter, the present invention will be described in detail.

The present invention provides a carbon nanotube array including nometallic carbon nanotubes and a process for producing the same. Inaddition, the present invention provides a material and an electronicdevice formed with a carbon nanotube array including no metallic carbonnanotubes.

In the present invention, the expression “including no metallic carbonnanotubes” means that the carbon nanotube array does not have propertiesof metallic carbon nanotubes. Specifically. “A including no metalliccarbon nanotubes” means that the electrical conductivity of “A” does notexhibit metallic properties, more specifically, semiconductorproperties.

Hereinafter, a process for producing a carbon nanotube array includingno metallic carbon nanotubes and the carbon nanotube array will besequentially described.

<Process for Producing Carbon Nanotube Array>

In the present invention, a carbon nanotube array including no metalliccarbon nanotubes is produced from a carbon nanotube array in whichmetallic carbon nanotubes and semiconducting carbon nanotubes arehorizontally aligned.

The process has the following steps.

That is, the process for producing a carbon nanotube array according tothe present invention includes: (A) a step of preparing a carbonnanotube array in which metallic carbon nanotubes and semiconductingcarbon nanotubes are horizontally aligned; (B) a step of forming anorganic layer on the carbon nanotube array; (C) a step of applyingvoltage to the horizontally aligned carbon nanotube array in a long axisdirection of the carbon nanotubes constituting the carbon nanotube arrayin the air; and (D) a step of removing the organic layer. After the (C)step is completed, the carbon nanotube array is free from metalliccarbon nanotubes.

<<Step (A)>>

Step (A) is a step of preparing a carbon nanotube array in whichmetallic carbon nanotubes and semiconducting carbon nanotubes arehorizontally aligned.

The carbon nanotube array in which metallic carbon nanotubes andsemiconducting carbon nanotubes are horizontally aligned can be producedby a conventionally known process. Although the process is not limitedto the following processes, for example, a method using a single crystalsubstrate having an R-cut surface described in WO2011/108545, whichpartially matches with the process of the present inventors of thepresent invention, a method using a SiO₂ single crystal substrate havinga ST-cut surface, a method using a sapphire substrate having an R-cutsurface, and a method using single crystal substrate having a step maybe used.

The carbon nanotube array to be prepared in Step (A) has metallic carbonnanotubes and semiconducting carbon nanotubes. The carbon nanotube arraymay include carbon nanotubes having other properties, for example, acarbon nanotube which is a metallic carbon nanotube but has defects andis thereby formed into a semiconductor-like carbon nanotube. However, itis preferable to suppress the amount of the carbon nanotube having otherproperties contained as much as possible in the case of using anelectronic material or the like.

In Steps (B) to (D), which will be described later, the length of eachsemiconducting carbon nanotube in the carbon nanotube array does notchange. Accordingly, the length of each semiconducting carbon nanotubein the carbon nanotube array in Step (A) may be 10 μm or more,preferably 100 μm or more, and more preferably 1,000 μm or more. In Step(A), when the length of each semiconducting carbon nanotube is set tothe above length, the carbon nanotube array having the above length canbe easily produced. In addition, a material having the carbon nanotubearray can be easily produced in large quantity. Further, using thecarbon nanotube array, an integrated circuit in which a large number ofFETs are also arranged in the axial direction of the array can beproduced.

In Steps (B) to (D), which will be described later, particularly, inStep (C), the metallic carbon nanotubes in the carbon nanotube array areremoved, but the density of the semiconducting carbon nanotubes does notchange. Accordingly, the density of the semiconducting carbon nanotubesin the carbon nanotube array in Step (A) is 1 line/μm or more,preferably 3 lines/μm or more, more preferably 10 lines/μm or more, andmore preferably 30 lines/μm or more.

In Steps (A) to (D), a substrate may be provided or may not be providedunder the carbon nanotube array. However, from the viewpoint of goodhandleability in Steps (A) to (D) and ease of easily using the carbonnanotube array obtained after Step (D) is performed for a material, itis preferable that a substrate is provided under the carbon nanotubearray.

The substrate may be a substrate (first substrate) used for obtaining acarbon nanotube array in which metallic carbon nanotubes andsemiconducting carbon nanotubes are horizontally aligned or may beanother substrate (second substrate) that is different from the firstsubstrate. That is, in the case of using the second substrate, the arraymay be moved onto from the first substrate used for obtaining the carbonnanotube array to the second substrate. As a method for moving the arrayfrom the first substrate to the second substrate, methods described inL. Jiao, B. Fan, X. Xian, Z. Wu, J. Zhang, and Z. Liu, J. Am. Chem. Soc.130, 12612 (2008), P. Zhao, B. Hou, X. Chen, S. Kim, S. Chiashi, E.Einarsson, S. Maruyama, “Investigation of Non-Segregation GrapheneGrowth on Ni via Isotope-Labeled Alcohol Catalytic Chemical VaporDeposition”, Nanoscale, (2013), 5, 6530-653, and the like may be used.The method is not limited to these methods.

<<Step (B)>>

Step (B) is a step of forming an organic layer on the carbon nanotubearray prepared in Step (A) above.

In Step (C), which will be described later, the organic layer exhibitsan effect of maintaining a combustion reaction of the metallic carbonnanotube. Since the organic layer more easily burns than the carbonnanotube, the organic layer can support the combustion. It is consideredthat the combustion reaction of each metallic carbon nanotube isconducted in the following steps while the combustion reaction issupported by combustion of the organic layer. First, the carbon nanotubetransports combustion heat at the end portion in the axial direction.The organic layer is heated by the transported combustion heat.Combustion starts in the organic layer of the heated portion by applyingthe combustion heat. The organic layer in which combustion has startedapplies the heat to the carbon nanotube again and combustion starts at aportion of the carbon nanotube to which heat is applied. By repeatingthe above steps, the combustion reaction of each metallic carbonnanotube is maintained.

The organic layer is a layer which exhibits the above effect and as longas an organic substance is used to form the layer, the organic substanceis not particularly limited. Only one or wo or more organic substancesmay be used.

As long as the organic layer exhibits the above effect, the layer may beformed on the carbon nanotube array in any form. It is preferable thatthe organic layer is formed so as to cover the entire carbon nanotubearray.

As long as the organic layer exhibits the above effect, the thicknessthereof is not particularly limited. For example, the thickness may be 3to 1,000 nm, preferably 10 to 100 nm and more preferably 20 to 60 nm.

The thermal diffusion coefficient of the organic substance may be 2×10⁻⁷m²/s or less, preferably 1×10⁻⁷ m²/s or less, and more preferably0.2×10⁻⁷ m²/s or less.

It is preferable that the organic substance has good heat retention toexhibit the above effect.

The organic layer may be a layer particularly made of onlyα,α,α′-tris(4-hydroxyphenyl)-1-ethyl-4-isopropylbenzene or a layer madeof only poly(methyl methacrylate).

The organic layer varies depending on an organic substance to be used,the molecular weight thereof, and the like. The layer can be obtained byapplying a solution of an organic substance to be used so as to coverthe entire carbon nanotube array by a conventionally known method.Although the conventional known method is not limited to the followingmethods, for example, spin coating, heat resistance deposition, and thelike may be used.

<<Step (C)>>

Step (C) is a step of applying voltage to the horizontally alignedcarbon nanotube array provided with the organic layer obtained in Step(B) above in the long axis direction of the carbon nanotubesconstituting the carbon nanotube array in the air. When Step (C) iscompleted, the carbon nanotube array is free from the metallic carbonnanotubes.

In Step (C), voltage is applied to the carbon nanotube array in whichmetallic carbon nanotubes and semiconducting carbon nanotube arehorizontally aligned. The voltage application direction is a directionalong the long axis direction of the carbon nanotubes constituting thecarbon nanotube array and it does not matter whether the direction isnormal or revered. Since the voltage pplied, an electrode may beappropriately provided.

The voltage is set such that a current flows only into the metalliccarbon nanotubes in the carbon nanotube array. Thus, while the metalliccarbon nanotubes are heated by self Joule heating, heat generation doesnot occur in the semiconducting carbon nanotubes.

In the above NPL 1, since the metallic carbon nanotubes are broken dueto self Joule heating and further combustion reaction does not proceed,the broken metallic carbon nanotubes remain. However, in Step (C) of thepresent invention, due to the presence of the organic layer, the effectof maintaining the combustion reaction of the metallic carbon nanotubeis exhibited. Due to this effect, it is considered that the metalliccarbon nanotubes burn over the entire length and the carbon nanotubearray is free from the metallic carbon nanotubes.

The voltage application in Step (C) is performed in the air in contrastwith “in vacuum or in an inert gas such as nitrogen” in NPL 2 using“thermocapillary flow”. In order to increase the yield rate of thecarbon nanotube array including no metallic carbon nanotubes, it ispreferable to perform Step (C) in the air having a high steam pressureas much as possible within a range not causing dew condensation.

The voltage application in Step (C) can be completed by monitoring thecurrent at the time of the voltage application. In Step (C), the currentis allowed to flow only into the metallic carbon nanotubes. When thewhole metallic carbon nanotubes are burned out, the current becomes zeroand thus the voltage application can be completed at the time when thecurrent becomes zero or after few minutes has passed from the zerocurrent, that is, Step (C) can be completed.

<<Step (D)>>

Step (D) is a step of removing the organic layer.

Step (D) is dependent on an organic substance to be used for the organiclayer. For example, an organic substance may be dissolved and removed byusing a solvent for dissolving the organic substance. For example, inthe case of using a layer made of onlyα,α,α′-tris(4-hydroxyphenyl)-1-ethyl-4-isopropylbenzene for the organiclayer, as a good solvent for the layer, for example, acetone or the likeis preferably used. In the case of using a layer made of onlypoly(methyl methacrylate) for the organic layer, as a good solvent forthe layer, for example, acetone or the like is preferably used.

The process for producing the carbon nanotube array according to thepresent invention having Steps (A) to (D) may include steps other thanSteps (A) to (D) above. Examples of other steps include an observationstep with an electron microscope (SEM), and an observation step usingRaman spectroscopy.

It is possible to obtain a carbon nanotube array including no metalliccarbon nanotubes by performing Steps (A) to (D) of the process forproducing the carbon nanotube array according to the present invention.Hereinafter, the carbon nanotube array including no metallic carbonnanotubes will be described.

<Carbon Nanotube Array Including No Metallic Carbon Nanotubes>

The carbon nanotube array of the present invention is a carbon nanotubearray including no metallic carbon nanotubes. The semiconducting carbonnanotubes constituting the carbon nanotube array are horizontallyaligned at a density of 1 line/μm or more. In addition, the density ispreferably 3 lines/μm or more, more preferably 10 lines/μm or more, andstill more preferably 30 lines/μm or more.

In contrast, the semiconducting carbon nanotubes are horizontallyaligned preferably at a density of 1,000 lines/μm or less, morepreferably at a density of 500 lines/μm or less, and most preferably ata density of 250 lines/μm or less.

By setting the density of the semiconducting carbon nanotubes to bewithin the above range, in the case of forming a field effect transistor(FET) with the carbon nanotube array including no metallic carbonnanotubes, electrolytic concentration on the semiconducting carbonnanotubes is easily achieved.

In NPL 1, the broken metallic carbon nanotubes remain. However, in thecarbon nanotube array of the present invention, the broken metalliccarbon nanotubes do not remain. That is, it is possible to provide acarbon nanotube array including no metallic carbon nanotubes. Herein, itis possible to confirm that the metallic carbon nanotubes “do notremain” from the fact that the metallic carbon nanotubes are notdetected in analysis through a “SEM image and the Raman spectroscopy”,which will be described later. In NPL 2, since “thermocapillary flow” isused, the density of the semiconducting carbon nanotubes is only about 1line/3 μm. In contrast, it is possible to increase the density of thesemiconducting carbon nanotubes in the carbon nanotube array of thepresent invention.

The length of each semiconducting carbon nanotube of the carbon nanotubearray may be 10 μm or more, preferably 100 μm or more, and morepreferably 1,000 μm or more.

In NPL 1, the length of each semiconducting carbon nanotube of thecarbon nanotube array including no metallic carbon nanotubes is 100 nmat most. Therefore, it is not possible to obtain a carbon nanotubehaving the same length as the carbon nanotube array of the presentinvention.

When the length of each semiconducting carbon nanotube of the carbonnanotube array is set as described above, a material having the carbonnanotube array can be easily produced in a large quantity. Further, whenthe carbon nanotube array is used, an integrated circuit in which alarge number of FETs are also arranged in the axial direction of thearray can be produced.

The carbon nanotube array of the present invention is free from metalliccarbon nanotubes. Therefore, in the case of forming a field effecttransistor (FET) with the carbon nanotube array, the ON/OFF ratio of theFET may be 10,000 or more, preferably 100,000 or more, and morepreferably 1,000,000 or more.

<Material and Electronic Device Having Carbon Nanotube Array>

The material of the present invention has the above-described carbonnanotube array. Although the material is not limited to the followingexamples, examples thereof include an electronic material, an opticalmaterial, or an electrochemical material.

The electronic device of the present invention has the above-describedcarbon nanotube array. Although the electronic device is not limited tothe following examples, examples thereof include a field effecttransistor (FET), a solar cell, a chemical sensor, a photosensor, anoptical element, or a terahertz sensor.

Hereinafter, although the present invention is further described indetail based on examples, the present invention is not limited to theexamples.

EXAMPLES Example 1

<a. Horizontally Aligned Carbon Nanotube Array Having s-CNTs and m-CNTs>

According to methods described in WO2011/108545, S. Chiashi, H. Okabe,T. Inoue, J. Shiomi, T. Sato, S. Kono, M. Terasawa, S. Maruyama*,“Growth of Horizontally Aligned Single-Walled Carbon Nanotubes on theSingular R-Plane (10-11) of Quartz”, J. Phys. Chem. C, (2012), 116,6805-6808, and T. Inoue, D. Hasegawa, S. Badar, S. Aikawa, S. Chiashi,S. Maruyama, “Effect of Gas Pressure on the Density of HorizontallyAligned Single-Walled Carbon Nanotubes Grown on Quartz Substrates”, J.Phys. Chem. C, (2013), 117, (22), 11804-11810, a horizontally alignedcarbon nanotube array having s-CNTs and m-CNTs was prepared.

Specifically, using a crystal substrate having an r-cut surface(manufactured by Hoffman Materials Inc.), a resist pattern was formed onthe substrate by photolithography. A catalyst was deposited on theentity of a substrate provided with a resist by vacuum deposition andthen the resist was removed so that a catalyst (Fe metal) pattern wasformed on the substrate.

The substrate having the catalyst (Fe metal) pattern was used to obtaina horizontally aligned carbon nanotube array having s-CNTs and m-CNTs byan alcohol CVD method.

The details will be described below. First, the substrate having thecatalyst (Fe metal) pattern was placed in a chamber and the inside ofthe chamber was evacuated. Then, an Ar gas was allowed to flow at a flowrate of 300 sccm for 5 minutes. Next, an Ar/H₂ mixed gas was allowed toflow at a flow rate of 300 sccm, and the pressure in the chamber was setto 40 kPa. Further, the temperature in the chamber was increased to 800°C. for 30 minutes and the temperature was maintained for 10 minutes. Theinside of the chamber was evacuated again while maintaining thetemperature. Then, ethanol as a carbon source was allowed to flow at aflow rate of 50 sccm, an Ar/H₂ mixed gas for adjusting the flow rate wasallowed to flow at a flow rate of 500 sccm, and the pressure was set to1.4 kPa. After 15 minutes had passed, a horizontally aligned carbonnanotube array was synthesized.

The obtained horizontally aligned carbon nanotube array has s-CNTs andm-CNTs both horizontally aligned. When the length of each carbonnanotube of the horizontally aligned carbon nanotube array was observedwith an electron microscope (SEM), the average length thereof was 30 μm.In addition, the density of the horizontally aligned s-CNTs was 1 to 4lines/μm.

<b. Transfer of Horizontally Aligned Carbon Nanotube Array to p-Type SiSubstrate>

The horizontally aligned carbon nanotube array formed on theabove-described crystal substrate having an r-cut surface wastransferred to a p-type Si substrate via poly(methyl methacrylate)(PMMA).

Specifically, an anisole solution (10 wt %) of PMMA was applied on thehorizontally aligned carbon nanotube array formed on the above-describedcrystal substrate having an r-cut surface by spin coating and a PMMAfilm was formed on the horizontally aligned carbon nanotube array. Next,the crystal substrate having the horizontally aligned carbon nanotubearray and provided with the PMMA film was immersed in a 1 M aqueouspotassium hydroxide solution. Then, the immersion state was maintainedfor a while, and then the PMMA film was peeled off in the aqueoussolution. As a result, the horizontally aligned carbon nanotube arraywas transferred onto the PMMA film. Then, the obtained PMMA film wasattached to a p-type Si substrate such that the side of the obtainedPMMA film having the horizontally aligned carbon nanotube array wasbrought into contact with the p-type Si substrate. Thereafter, the PMMAfilm was removed with acetone. Further, the horizontally aligned carbonnanotube array was transferred to the p-type Si substrate by annealingat 350° C. for 3 hours in vacuum.

When the horizontally aligned carbon nanotube array on the p-type Sisubstrate was observed with an SEM, the carbon nanotube array exhibitedthe same properties before being transferred. In addition, when thecarbon nanotube array was observed with an SEM, the average length ofeach carbon nanotube had the same value before being transferred, andthe density of the horizontally aligned s-CNTs had the same value beforebeing transferred.

<c. Arrangement of Electrode and Measurement of ON/OFF Ratio of FieldEffect Transistor (FET)>

Electrodes were arranged on the horizontally aligned carbon nanotubearray provided on the obtained p-type Si substrate. The electrode isused for the following reasons. First, the electrode is used as anelectrode (source electrode or drain electrode) of a field effecttransistor (FET). In the case of removing the m-CNTs, the electrode isalso used as an electrode used for voltage application when the m-CNTsare removed.

The electrodes were provided on the side of the p-type Si substratehaving the horizontally aligned carbon nanotube array so as to beorthogonal to each carbon nanotube of the horizontally aligned carbonnanotube array in the long axis direction. The electrodes arranged asdescribed above respectively function as a source electrode and a drainelectrode in the FET.

More specifically, Ti/Pd (5/50 nm) was used for an electrode metal and aresist patterned into an electrode having a desired shape byphotolithography. The substrate having the resist was placed in a filmforming chamber and plasma was generated under the conditions of 0.2 Pa,an Ar gas flow rate of 10 sccm, and an output of 100 W. Thus, electrodeswere provided on the substrate. In addition, an electrode whichfunctions as a gate electrode in the FET was also provided on the sideof the p-type Si substrate not having the horizontally aligned carbonnanotube array.

<<c-1. Measurement of ON/OFF Ratio in the Case of Forming Field EffectTransistor (FET) Using Carbon Nanotube Array Having m-CNTs and s-CNTs>>

The ON/OFF ratio in the case of forming a FET with the carbon nanotubearray having m-CNTs and s-CNTs and provided with the electrodes wasmeasured. The result is indicated by “Before” of FIG. 1.

From “Before” of FIG. 1, it is found that the ON/OFF ratio is 1 order.From the result, it is found that the carbon nanotube array includesm-CNTs and thus a short circuit occurs due to the m-CNTs.

<d. Formation of Layer Made ofα,α,α-Tris(4-Hydroxyphenyl)-1-Ethyl-4-Isopropylbenzene>

A layer made of α,α,α-tris(4-hydroxyphenyl)-1-ethyl-4-isopopylbenzene(represented by the following Formula (I)) was formed on the carbonnanotube array having m-CNTs and s-CNTs provided with the electrodes byvacuum deposition, which was obtained in the above <c.>.

Specifically, the substrate obtained in the above <c.> was arranged on astage. A sample ofα,α,α-tris(4-hydroxyphenyl)-1-ethyl-4-isopropylbenzene was placed on atungsten boat connecting between the electrodes. The stage and the boatwere covered with the chamber and the inside of the chamber wasevaluated to 2.0×10⁻³ Pa using a rotary pump and an oil diffusion pump.Then, voltage was applied between the electrodes, a current of about 20A was allowed to flow into the boat, and the sample was evaporated to bedeposited on the substrate. It was confirmed that the film thickness was60 nm (0.06 μm) with a crystal vibrator arranged in the chamber.

<e. Voltage Application>

Voltage was applied to the carbon nanotube array having m-CNTs ands-CNTs, provided with the electrodes, and obtained in the above <d.> inthe air.

Specifically, as shown in FIG. 2, one of the electrodes provided on thecarbon nanotube array having m-CNTs and s-CNTs was set to a sourceelectrode and the other one was set to a drain electrode. The sourceelectrode was grounded and a drain voltage was applied such that acurrent flows from the drain electrode to the source electrode. As agate voltage, while setting a direction in which the current flows fromthe gate electrode to the source electrode as a positive direction, +10V was applied. A distance between the drain electrode and the sourceelectrode was 16.4 μm.

The drain voltage was applied at a voltage increase rate of 0.67 V/min,the current accompanying the voltage application was measured and afterabout 1 minute had passed from the time when the current value becomeszero, the voltage application was terminated. The voltage at the time oftermination was about 40 V.

<f. Removal of Layer Made ofα,α,α,-Tris(4-Hydroxyphenyl)-1-Ethyl-4-Isopropylbenzene>

The layer made of α,α,α-tris(4-hydroxyphenyl)-1-ethyl-4-isopropylbenzeneon the substrate obtained in the above <e.> was removed with acetone.

Specifically, the substrate obtained in the above <e.> was immersed inacetone for several minutes and then rinsed with isopropanol anddistilled water. Thereafter, the layer made ofα,α,α-tris(4-hydroxyphenyl)-1-ethyl-4-isopropylbenzene was removed bydrying the substrate.

<g. Carbon Nanotube Array Obtained in Above f. and Measurement of ON/OFFRatio in the Case of Forming FET Using Same>

The substrate having the carbon nanotube array obtained in the above<f.> is provided with a gate electrode, a source electrode, and a drainelectrode. The ON/OFF ratio of the FET having the carbon nanotube arraywas measured. The result is indicated by “After” in FIG. 1.

From “After” in FIG. 1, it is found that the ON/OFF ratio is 10⁴ order.From the result, the carbon nanotube array is free from m-CNTs and madeup of only s-CNTs.

In addition, the carbon nanotube array obtained in the above <f.> wascompared with the carbon nanotube array obtained before voltageapplication in the above <e.>. When comparing the carbon nanotubearrays, SEM images and Raman spectroscopy were used. The results areshown in FIGS. 3 and 4, respectively.

<<SEM Image>>

FIG. 3 shows SEM images in which the carbon nanotube array obtained inthe above <f.> (indicated by “After”) is compared with the carbonnanotube array obtained before voltage application in the above <e.>(indicated by “Before”). From the SEM images, it is found that the m-CNTpresent within a distance of 1 μm between s-CNTs is removed. From theresult, it is found that the density of the s-CNTs of the carbonnanotube array obtained in the above <f.> is 1 line/μm.

<<SEM Image and Raman Spectroscopy

FIG. 4 shows SEM images, that is, SEM images of the carbon nanotubearray obtained in the above <f.> (indicated by “After”) on the rightside and the carbon nanotube array obtained before voltage applicationin the above <e.>(indicated by “Before”) are shown on the right side andresults of measuring Raman scattering of spots shown in the SEM imagesby Raman spectroscopy (“After” and “Before” are the same as describedabove) on the left side.

From the measurement results shown in FIG. 4 by the Raman spectroscopy,it is found that in the carbon nanotube array obtained in the above <f.>(indicated by “After”), the peak in a range of 1,500 to 1,650 cm⁻¹ isnot observed. In addition, it is found that CNTs are not present in thecorresponding spot from the SEM image. From these results, it is foundthat the carbon nanotube array obtained from the above <f.> (indicatedby “After”) is free from m-CNTs.

From the results of the ON/OFF ratio of the FET in the above <g.>, andSEM images, and Raman spectroscopy, it is found that the carbon nanotubearray obtained in the above <f.> is free from m-CNTs. In the above <f.>,the layer made of α,α,α-tris(4-hydroxyphenyl)-1-ethyl-4-isopropylbenzeneis simply removed. Therefore, it is found that at the tune when voltageapplication is terminated in the above <e.>, the carbon nanotube arrayis free from m-CNTs.

It is found that the carbon nanotube array obtained in the above <f.> isuseful as a FET from the result of the ON/OFF ratio of the FET.

Example 2

<a.> to <g.> in Example 1 were performed except that instead of <d.Formation of Layer Made ofα,α,α-Tris(4-Hydroxyphenyl)-1-Ethyl-4-Isopropylbenzene> in Example 1,<d′. Formation of Layer made of PMMA> was used and instead of <f.Removal of Layer Made ofα,α,α-Tris(4-Hydroxyphenyl)-1-Ethyl-4-Isopropylbenzene>, <f′. Removal ofLayer Made of PMMA> was used.

<d′. Formation of Layer Made of PMMA>

A 1 wt % anisole solution of PMMA was prepared. The solution was appliedto the carbon nanotube array having m-CNTs and s-CNTs by spin coatingand then the solution was removed at 120° C. Thus, a layer made of PMMAwas formed on the carbon nanotube array having m-CNTs and s-CNTs. Whenthe thickness of the layer was measured using a stylus type surfaceprofiler (Dektak XT, manufactured by ULVAC, Inc.), it was confirmed thatthe thickness is 20 to 50 nm.

<f′. Removal of Layer made of PMMA>

The layer made of PMMA on the substrate obtained in the above <e.> wasremoved with acetone.

Specifically, the substrate obtained in the above <e.> was immersed inacetone for several minutes and rinsed with isopropanol and distilledwater. Thereafter, the layer made of PMMA was removed by drying thesubstrate.

From the results of the ON/OFF ratio measurement of the FET (10,000),SEM image observation, and AFM measurement (none of these are shown inthe drawing), it was found that the carbon nanotube array obtained inExample 2 is free from m-CMTs similar to Example 1. In addition, it wasfound that the carbon nanotube array obtained in Example 2 was useful asa FET from the results of the ON/OFF ratio of the FET.

1. A carbon nanotube array including no metallic carbon nanotubes,wherein semiconducting carbon nanotubes are horizontally aligned at adensity of 1 line/μm or more.
 2. The carbon nanotube array according toclaim 1, wherein a density of the semiconducting carbon nanotubes is1,000 lines/μm or less.
 3. The carbon nanotube array according to claim1, wherein a length of each semiconducting carbon nanotube of the carbonnanotube array is 10 μm or more.
 4. The carbon nanotube array accordingto claim 1, wherein in a case of forming a field effect transistor (FET)with the carbon nanotube array, an ON/OFF ratio of the FET is 10,000 ormore.
 5. A material including the carbon nanotube array according toclaim
 1. 6. An electronic device including the carbon nanotube arrayaccording to claim
 1. 7. A process for producing a carbon nanotube arraycomprising: (A) a step of preparing a carbon nanotube array in whichmetallic carbon nanotubes and semiconducting carbon nanotubes arehorizontally aligned; (B) a step of forming an organic layer on thecarbon nanotube array; (C) a step of applying voltage to thehorizontally aligned carbon nanotube array in a long axis direction ofthe carbon nanotubes constituting the carbon nanotube array in the air;and (D) a step of removing the organic layer.
 8. The process forproducing a carbon nanotube array according to claim 7, wherein theorganic substance in the (B) step has a thermal diffusion coefficient of2×10⁻⁷ m²/s or less.
 9. The process for producing a carbon nanotubearray according to claim 7, wherein the organic layer in the (B) step isa layer made of onlyα,α,α′-tris(4-hydroxyphenyl)-1-ethyl-4-isopropylbenzene or a layer madeof only poly(methyl methacrylate).
 10. The process for producing acarbon nanotube array according to claim 7, wherein the semiconductingcarbon nanotubes are horizontally aligned at a density of 1 line/μm ormore.
 11. The process for producing a carbon nanotube array according toclaim 7, wherein a length of the semiconducting carbon nanotube is 10 μmor more.
 12. A process for producing a field effect transistor (FET)using a carbon nanotube array that is produced using the process forproducing a carbon nanotube array according to claim 7, wherein anON/OFF ratio is 10,000 or more.